Milling & Mixing

Main function

High-energy milling, mixing and mechanical alloying of materials by impact and friction to produce uniform micro–nano powders

Technical specifications

• Type: Planetary ball mill (4 jar stations)
• Revolution speed: 35 – 405 rpm
• Rotation speed: 70 – 810 rpm
• Maximum total grinding speed: 1215 rpm
• Grinding jar capacity: 4 jars × 100 / 250 / 500 mL
• Maximum loading per jar: not exceeding 2/3 of the jar volume
• Jar & ball materials: zirconia, corundum, vacuum stainless steel, etc.
• Cooling: air chiller system, jar temperature 10 – 15 °C
• Operation in real clip: https://www.facebook.com/share/v/1Bxwt1kMHA/
• Funding source: Tuan Anh

Purpose of use

EN: Milling, mixing and mechanical alloying of materials by high-energy impact to produce uniform micro–nano powders with controlled composition, especially for advanced materials such as thermoelectric alloys, semiconductors, oxide ceramics and other functional materials. The powders are prepared for sintering, hot pressing or sputtering. Chiller-cooled jars minimize material degradation, and the solvent-free process supports green synthesis, reducing chemicals and research time.
VI: Nghiền, trộn và hợp kim hóa cơ học vật liệu bằng cơ chế va đập năng lượng cao để chế tạo bột mịn kích thước micro–nano đồng đều, kiểm soát thành phần, đặc biệt cho các vật liệu tiên tiến như hợp kim nhiệt điện, vật liệu bán dẫn, gốm oxit và các vật liệu chức năng khác. Bột sau nghiền phục vụ cho thiêu kết, ép nóng hoặc phún xạ. Hệ làm mát bằng chiller giúp hạn chế biến đổi vật liệu, và quy trình không dùng dung môi hỗ trợ tổng hợp xanh, giảm hóa chất và rút ngắn thời gian nghiên cứu.

Main function

Fine wet/dry grinding, mixing and homogenizing of powders and slurries in rotating jars with grinding media

Technical specifications

• Model: Mulini Serie "S" rapid laboratory ball mill
• Manufacturer: Ceramic Instruments S.r.l. (Italy)
• Type: High-speed laboratory jar ball mill with protective safety enclosure
• Grinding modes: dry powder grinding and wet slurry milling
• Jar capacity: interchangeable jars, 300 – 1500 mL
• Jar materials: sintered alumina (Al2O3), technical porcelain or stainless steel
• Grinding media: alumina or zirconia balls
• Control: analog console with main power switch, emergency stop and start button
• Process timer: electromechanical timer FIBER T45, 0 – 60 min, automatic cycle shut-off
• Safety: spring-loaded latch cover with automatic safety interlock during operation
• Power supply: AC 230 V, 50 Hz

Purpose of use

EN: Rapid size reduction of powders, breaking of agglomerates and uniform mixing of precursor and metal oxide powders (dry or in slurry) for research and laboratory quality control. High-speed rotation makes the grinding media cascade inside the jar, producing impact and shear forces within an enclosed, soundproof safety cabinet.

VI: Tán mịn nhanh bột, đánh tơi khối vón cục và phối trộn đồng đều bột tiền chất và oxit kim loại (khô hoặc dạng huyền phù) phục vụ nghiên cứu và kiểm soát chất lượng trong phòng thí nghiệm. Quay tốc độ cao khiến các viên bi chuyển động va đập và tạo lực cắt xé trong cối nghiền, đặt trong buồng cách âm an toàn.