Main function

High-energy milling, mixing and mechanical alloying of materials by impact and friction to produce uniform micro–nano powders

Technical specifications

• Type: Planetary ball mill (4 jar stations)
• Revolution speed: 35 – 405 rpm
• Rotation speed: 70 – 810 rpm
• Maximum total grinding speed: 1215 rpm
• Grinding jar capacity: 4 jars × 100 / 250 / 500 mL
• Maximum loading per jar: not exceeding 2/3 of the jar volume
• Jar & ball materials: zirconia, corundum, vacuum stainless steel, etc.
• Cooling: chiller system, jar temperature 10 – 15 °C
• Operation in real clip: https://www.facebook.com/share/v/1Bxwt1kMHA/

Purpose of use

EN: Milling, mixing and mechanical alloying of materials by high-energy impact to produce uniform micro–nano powders with controlled composition, especially for advanced materials such as thermoelectric alloys, semiconductors, oxide ceramics and other functional materials. The powders are prepared for sintering, hot pressing or sputtering. Chiller-cooled jars minimize material degradation, and the solvent-free process supports green synthesis, reducing chemicals and research time.
VI: Nghiền, trộn và hợp kim hóa cơ học vật liệu bằng cơ chế va đập năng lượng cao để chế tạo bột mịn kích thước micro–nano đồng đều, kiểm soát thành phần, đặc biệt cho các vật liệu tiên tiến như hợp kim nhiệt điện, vật liệu bán dẫn, gốm oxit và các vật liệu chức năng khác. Bột sau nghiền phục vụ cho thiêu kết, ép nóng hoặc phún xạ. Hệ làm mát bằng chiller giúp hạn chế biến đổi vật liệu, và quy trình không dùng dung môi hỗ trợ tổng hợp xanh, giảm hóa chất và rút ngắn thời gian nghiên cứu.